Fatigue characteristics of bearing steel in very high cycle fatigue

Chang-Min, Suh
The Journal of Mechanical Science and Technology, vol. 23, no. 2, pp.420-425, 2009

Abstract : Very high cycle fatigue (VHCF) tests were carried out to find the fatigue characteristics of a super-long life range by using a cantilever type rotational bending fatigue test machine on three kinds of specimens in bearing steel which were quenched and tempered in air (A: non-shot peened and B: shot peened after heat treatment) and under vacuum environment(C: non-shot peened) in this study. S-N curves obtained from the VHCF tests of the B and C specimens tend to come down again in the super-long life (109 cycles) range due to fish-eye type cracking, while most of the A and B specimens were fractured by surface defects such as scratches and slip lines. This duplex S-N behavior of bearing steel has to be reviewed by the change of the fracture modes.

Keyword : Very high cycle fatigue (VHCF); Rotational bending fatigue test; Shot peening; Fatigue characteristic; Fish-eye crack; Giga

 
 
 
 
 
JMST Editorial Office: #702 KSTC New Bldg, 22 7-gil, Teheran-ro, Gangnam-gu, Seoul 06130, Korea
TEL: +82-2-501-3605, E-mail: editorial@j-mst.org
JMST Production Office: #702 KSTC New Bldg, 22 7-gil, Teheran-ro, Gangnam-gu, Seoul 06130, Korea
TEL: +82-2-501-6056, FAX: +82-2-501-3649, E-mail: editorial@j-mst.org